BlastMate PPS-CF
TECHNICAL DATA SHEET
BlastMate PPS-CF is a 10% carbon fiber reinforced polyphenylene sulfide (PPS) filament made with LUVOCOM® 3F resin from LEHVOSS Group. PPS is a semicrystalline, high-performance polymer used in numerous challenging applications in various industries. This material has an outstanding price-to-performance ratio with exceptional strength, stiffness, temperature, chemical and wear resistance. PPS is suitable in many cases instead of higher priced super polymers as PAEKs (PEEK, PEKK).
Physical properties | Unit | Typical value | Test method |
Density | g/cm³ | 1.3 | ASTM D792 (ISO 1183) |
Heat distortion temperature | °C | 245 | ASTM D648 (ISO 75)1.8MPa |
°C | 275 | ASTM D648 (ISO 75)0.45MPa | |
Melt temperature | °C | 280 | ISO 11357 |
Mechanical properties | |||
Tensile strength（X-Y） | MPa | 110 | ASTM D638(ISO 527) |
Elongation at break（X-Y） | % | 1.3 | ASTM D638(ISO 527) |
Bending strength（X-Y） | MPa | 180 | ASTM D790(ISO 178) |
Bending modulus（X-Y） | MPa | 9000 | ASTM D790(ISO 178) |
Young’s modulus X-Y) | MPa | 10000 | ISO527 |
Charpy impact strength（X-Y） | kJ/m² | 30 | ASTM D256(ISO 179) |
Recommended Printing Settings | Unit | Value | |
Printing temperature | ˚C | 340 | |
Nozzle material | - | Hardened steel | |
Bed temperature | ˚C | 100 | |
Layer thickness | mm | 0.2 | |
Printing speed | mm/s | 220 - 300 | |
Note:
Due to the large variety of machines, geometries, and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Build Plate PEI ✔ Carbon Fiber X
Flame Retardant Rate: VO
Applications
Prototype | Jig & fixture | Cover & housing | Functional parts | Automotive & automation | Defense & others |
✔ | ✔ | ✔ | ✔ | ✔ | ✔ |