BlastMate PET-CF
TECHNICAL DATA SHEET
BlastMate PET-CF is a carbon fiber reinforced PET filament. It has high stiffness, high hardness, high strength and strong wear resistance. Compared to PA-CF, it has the characters of easy printing, lower water absorption rate and lower risk of print head choking. Suitable for high performance structural parts, MRO, spare parts and mass customized production.
Physical properties | Unit | Typical value | Test method | |
Density | g/cm³ | 1.3 | ASTM D792 (ISO 1183) | |
Heat distortion temperature | °C | 112 | ASTM D648 (ISO 75)1.8MPa | |
°C | 148.8 | ASTM D648(ISO75)0.45MPa | ||
Melt temperature | °C | 249 | ISO 306 | |
Mechanical properties | ||||
Tensile strength（X-Y） | MPa | 92 | ASTM D638(ISO 527) | |
Elongation at break（X-Y） | % | 2 | ASTM D638(ISO 527) | |
Bending strength（X-Y） | MPa | 127 | ASTM D790(ISO 178) | |
Bending modulus（X-Y） | MPa | 5400 | ASTM D790(ISO 178) | |
Young’s modulus X-Y) | MPa | 5730 | ISO527 | |
Charpy impact strength（X-Y） | kJ/m2 | 6 | ASTM D256(ISO 179) | |
Recommended Printing Settings | Unit | Value | ||
Printing temperature | ˚C | 280 – 320 | ||
Nozzle material | - | Hardened steel | ||
Bed temperature | ˚C | 80 - 90 | ||
Layer thickness | mm | 0.2 | ||
Printing speed | mm/s | 220 - 300 |
Note:
Due to the large variety of machines, geometries, and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Build Plate PEI X Carbon Fiber ✔
Applications
Prototype | Jig & fixture | Cover & housing | Functional parts | Automotive & automation | Defense & others |
✔ | ✔ | ✔ | ✔ | ✔ | ✔ |