BlastMate PAHT-CF
TECHNICAL DATA SHEET
BlastMate PAHT-CF is made with high temperature Nylon combined with 15% high-rigidity carbon fiber, which has higher modulus, mechanical strength and rigidity. The continuous working temperature can reach up to 190°C. With the carbon fiber reinforcement, its dimensional stability is improved dramatically, and the risk of printing warping is significantly reduced. Suitable for printing large size products without warpage concern with Blast2 agile mfg platform
Physical properties | Unit | Typical value | Test method |
Density | g/cm³ | 1.15 | ASTM D792 (ISO 1183) |
Heat distortion temperature | °C | 121 | ASTM D648 (ISO 75)1.8MPa |
°C | 193 | ASTM D648 (ISO 75)0.45MPa | |
Melt temperature | °C | 231 | ISO 11357 |
Mechanical properties | |||
Tensile strength（X-Y） | MPa | 105 | ASTM D638(ISO 527) |
Elongation at break（X-Y） | % | 1.6 | ASTM D638(ISO 527) |
Bending strength（X-Y） | MPa | 151 | ASTM D790(ISO 178) |
Bending modulus（X-Y） | MPa | 6140 | ASTM D790(ISO 178) |
MPa | 7492 | ISO527 | |
Charpy impact strength（X-Y） | kJ/m² | 6.3 | ASTM D256(ISO 179) |
Recommended Printing Settings | Unit | Value | |
Printing temperature | ˚C | 300 – 320 | |
Nozzle material | - | Hardened steel | |
Bed temperature | ˚C | 70 - 80 | |
Layer thickness | mm | 0.2 | |
Printing speed | mm/s | 220 - 300 | |
Note:
Due to the large variety of machines, geometries, and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Build Plate PEI X Carbon Fiber ✔
Applications
Prototype | Jig & fixture | Cover & housing | Functional parts | Automotive & automation | Defense & others |
✔ | ✔ | ✔ | ✔ | ✔ | ✔ |