BlastMate ABS-CF20
TECHNICAL DATA SHEET
BlastMate ABS-CF20 customize ABS is odorless, high fluidity, and achieves high throughput printing with Blast2. At the same time, the high proportion of 20% carbon fiber filling ensures stronger mechanical properties and heat resistance of printed parts. BlastMate ASB-CF20's coating resin lower the abrasion of nozzle and increase the layer adhesion
Physical properties | Unit | Typical value | Test method | ||
Density | g/cm³ | 1.09 | ASTM D792 (ISO 1183) | ||
Heat distortion temperature | °C | 83 | ASTM D648 (ISO 75)1.8MPa | ||
°C | 90 | ASTM D648 (ISO 75)0.45MPa | |||
Melt Temperature | °C | 250 | ISO 11357 | ||
Mechanical properties | |||||
Tensile strength（X-Y） | MPa | 48.8 | ASTM D638(ISO 527) | ||
Elongation at break（X-Y） | % | 1.48 | ASTM D638(ISO 527) | ||
Bending strength（X-Y） | MPa | 80.2 | ASTM D790(ISO 178) | ||
Bending modulus（X-Y） | MPa | 4365 | ASTM D790(ISO 178) | ||
Young’s modulus X-Y) | MPa | 4606 | ISO527 | ||
Charpy impact strength（X-Y） | kJ/m2 | 8.12 | ASTM D256(ISO 179) | ||
Recommended Printing Settings | Unit | Value | |||
Printing temperature | ˚C | 250 – 270 | |||
Nozzle material | - | Hardened steel | |||
Bed temperature | ˚C | 100 – 110 | |||
Layer thickness | mm | 0.2 | |||
Printing speed | mm/s | 220 – 300 | |||
Note:
Due to the large variety of machines, geometries, and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Build Plate PEI ✔ Carbon Fiber X
Applications
Prototype | Jig & fixture | Cover & housing | Functional parts | Automotive & automation | Defense & others |
✔ | ✔ | ✔ | ✔ |