BlastMate PETG-GF
TECHNICAL DATA SHEET
BlastMate PETG-GF is a PETG material filled with chopped glass fibers, keep warping resistance, and improve the print quality of overhanging surface at the same time. BlastMate PETG-GF has good bending strength and high temperature resistance, suitable for application which need strength and high working temperature.
Physical properties | Unit | Typical value | Test method | ||
Density | g/cm³ | 1.3 | ASTM D792 (ISO 1183) | ||
Heat distortion temperature | °C | 68 | ASTM D648 (ISO 75)1.8MPa | ||
°C | 73 | ASTM D648(ISO 75)0.45MPa | |||
Melt temperature | °C | 230 | ISO 11357 | ||
Mechanical properties | |||||
Tensile strength（X-Y） | MPa | 48.8 | ASTM D638(ISO 527) | ||
Elongation at break（X-Y） | % | 3.8 | ASTM D638(ISO 527) | ||
Bending strength（X-Y） | MPa | 56.8 | ASTM D790(ISO 178) | ||
Bending modulus（X-Y） | MPa | 1730 | ASTM D790(ISO 178) | ||
Young’s modulus X-Y) | MPa | 2616 | ISO527 | ||
Charpy impact strength（X-Y） | kJ/m2 | 5.6 | ASTM D256(ISO 179) | ||
Recommended Printing Settings | Unit | Value | |||
Printing temperature | ˚C | 235 - 260 | |||
Nozzle material | - | Hardened steel | |||
Bed temperature | ˚C | 70 - 80 | |||
Layer thickness | mm | 0.2 | |||
Printing speed | mm/s | 220 - 300 | |||
Note:
Due to the large variety of machines, geometries, and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Build Plate PEI ✔ Carbon Fiber X
Applications
Prototype | Jig & fixture | Cover & housing | Functional parts | Automotive & automation | Defense & others |
✔ | ✔ | ✔ | ✔ |