TECHNICAL DATA SHEET
BlastMate PLApro has excellent mechanical properties and printing quality. No need to enclose the printing area or heat the platform during printing, which contributes to rapid prototyping and easy printing. The filament has 4 colors to choose without irritating odor. Also, Blast2 best fit extrusion strength mapping with extrusion efficiency, keep the high flow and avoid nozzle clogging at the same time.
Physical properties | Unit | Typical value | Test method | ||||
Density | g/cm³ | 1.24 | ASTM D792 (ISO 1183) | ||||
Heat distortion temperature | °C | 50 | ASTM D648(ISO75)0.45MPa | ||||
Melt temperature | °C | 155 | ISO 11357 | ||||
Mechanical properties | |||||||
Tensile strength（X-Y） | MPa | 53 | ASTM D638(ISO 527) | ||||
Elongation at break（X-Y） | % | 4.5 | ASTM D638(ISO 527) | ||||
Bending strength（X-Y） | MPa | 82 | ASTM D790(ISO 178) | ||||
Bending modulus（X-Y） | MPa | 3104 | ASTM D790(ISO 178) | ||||
Young’s modulus X-Y) | MPa | 2878 | ISO527 | ||||
Charpy impact strength（X-Y） | kJ/m2 | 14 | ASTM D256(ISO 179) | ||||
Recommended Printing Settings | Unit | Value | |||||
Printing temperature | ˚C | 200 – 230 | |||||
Nozzle material | - | Plated Copper | |||||
Bed temperature | ˚C | 40 - 60 | |||||
Layer thickness | mm | 0.2 | |||||
Printing speed | mm/s | 220-300 | |||||
Note:
Due to the large variety of machines, geometries, and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Build Plate PEI ✔ Carbon Fiber X
Applications
Prototype | Jig & fixture | Cover & housing | Functional parts | Automotive & automation | Defense & others |
✔ |